All Products
-
DavidGood company with nice service and high quality and high reputation. One of our reliable supplier , goods are delivered in time and nice package. -
John MorrisMaterial experts, rigorous processing, timely discovery of problems in design drawings and communication with us, thoughtful service, reasonable price and good quality, I believe we will have more cooperation. -
JorgeThank you for your good after-sales service. Excellent expertise and technical support helped me a lot. -
PetraThrough very good communication all problems solved, satisfied with my purchase -
Adrian HayterThe goods purchased this time are very satisfied, the quality is very good, and the surface treatment is very good. I believe we will order the next order soon.
Contact Person :
Nicole
Phone Number :
13186382597
Whatsapp :
+8613186382597
Corrosion Resistant Metal Gr1 Titanium Foil In Coil Rolled 0.01mm min. Thickness
Contact me for free samples and coupons.
Whatsapp:0086 18588475571
Wechat: 0086 18588475571
Skype: sales10@aixton.com
If you have any concern, we provide 24-hour online help.
xProduct Details
| Name | Corrosion Resistant Metal Gr1 Titanium Foil In Coil Rolled | Material | Pure Titanium |
|---|---|---|---|
| Grade | Gr1 | Shape | Foil,strip In Coil |
| Thickness | 0.01mm Min. | Width | 250mm |
| Surface | Polished | Process | Cold Rolled |
| Highlight | Gr1 Titanium Foil,Corrosion Resistant Titanium Foil,Coil Rolled Titanium Foil |
||
Product Description
The main difference between Gr1 and Gr2 lies in the content of iron, oxygen and nitrogen. Due to the different contents of the above elements, the strength is also quite different, especially the oxygen content. A difference of 0.01% in oxygen content will bring a strength difference of tens of MPa. Therefore, there are some differences in subsequent processing performance. However, for the corrosion resistance of the material, the two are almost equivalent. Generally speaking, pure titanium GR.1 and GR.2 are basically used to manufacture various working conditions with a temperature of -253 to 250°C and low stress.
National standards:
National standard: GB/T 3622
American standard: ASTM B265
Dimensions:
Thickness: ≤0.1mm
Width: ≤600mm
Length: customizable
Weight per roll: 0~100kg
Main ingredients:
| Chemistry composition % | |||||||||||||
| Designation | Chief component | Impurities maxmium | |||||||||||
| Ta | Nb | Fe | Si | Ni | W | Mo | Ti | Nb | O | C | H | N | |
| Gr1 | Remainder | / | 0.004 | 0.003 | 0.002 | 0.004 | 0.006 | 0.002 | 0.03 | 0.015 | 0.004 | 0.0015 | 0.002 |
| Gr2 | Remainder | / | 0.01 | 0.01 | 0.005 | 0.02 | 0.02 | 0.005 | 0.08 | 0.02 | 0.01 | 0.0015 | 0.01 |
Mechanical properties:
Tensile strength: 270Mpa ≤ ob ≤ 410Mpa, yield strength ob≥ 165Mpa: elongation: δ≥27%.
Supporting welding materials:ERTi-1.
Corrosion resistance:
Titanium has excellent corrosion resistance in alkaline solutions such as sulfuric acid, hydrochloric acid, nitric acid and sodium hydroxide, as well as in moisture and seawater. However, titanium cannot resist the corrosion of hydrofluoric acid.
Titanium is very stable in the atmosphere, and a dense oxide film is formed on the surface, which can maintain the metallic luster; but when heated to above 600℃, the oxide film loses its protective effect.
Application areas:Aerospace, plate heat exchangers, bellows compensators, expansion joints, seawater desalination, desulfurization and denitrification, chemical equipment and civilian tableware industries, etc.